Fe-Cr-Co alloy has a big advantage, namely its high Curie temperature, Tc = 680ºC for the left and right (Tc slightly different in different alloy grades) so that its temperature can reach 400ºC, reversible temperature coefficient is small, is -0.0128%ºC, the magnetic stability of the well for the high-precision components.

Shapes: Blocks, square rods, round rods, strips, wire
Sizes: Round rods of Dia. 2-70 mm
Strip of thickness 0.5-20 mm
Notes: Since FeCrCo alloys can be easily hot deformed and machined, there are practically no limitations of their shapes and sizes.
In particular, sheet blanks for further deep drawing of cups and washers for hysteresis motors and brakes, thin long rods (Dia 2-5 mm, L 110 mm), “cow magnets” (Dia 15-20 mm, L-50-70 mm), thin rings etc. are available

·What is the Fecrco Magnet?
Features: Iron, cobalt chromium magnet is the early 1970s, the new permanent magnetism materials. The magnetic cobalt nickel and aluminum, plane eight permanent magnet is extremely magnetization, plane and multipole magnetization mechanical processing, especially suitable for the advantages and complex shape of small size requirement, low magnetic components.

·Fecrco Magnet Usage
Fe - Cr - Spinodal decomposition Co alloy is according to the theory of Fe - in the alloy based on binary Cr plus Co, FeCrCo magnet in high form a single alpha, then, through the Spinodal decomposition form alpha 1 and 2, then the alpha tempering process, two phase composition difference, thus can achieve higher magnetic.